FCW M CrMo1
Description & applications
• Seamless high fill copper coated metal cored wire for gas metal arc welding
• Single and multiple pass welding of creep resisting steels alloyed with 1.25Cr-0.5Mo
• Optimal productivity by combining advantages of both seamless and seamed tubular wires
• HDM guaranteed < 4 ml/ 100g deposited metal on the whole parameter box
• No moisture pick up, excellent wire feeding properties, good weldability and low spatter
• Designed for service temperatures up to 550°C
APPLICATIONS
Welding creep-resisting steels of similar composition. Preheat 150-250°C and stress relieving 660 -700°C must be carried out.
Examples
Creep resisting steel EN 10028-2 13 CrMo 4-5
Creep resisting steel EN 10083-1 25 CrMo 4 EN 10222-2 14 CrMo 4-5
Case hardening steel DIN 17210 16MnCr5
Case hardening steel ISO/TR 15608: Group 5.1
Classification
| AWS A 5.28 | EN ISO 17634-A | EN ISO 17634-B | ASME IX Qualification |
|---|---|---|---|
| E80C-B2 H4 | T CrMo1 M M 1 H5 | T55T15-1M-1CM-H5 | QW-432 F-N° 6 / QW-442 A-N° 3 |
Typical weld metal composition (%)
| C | Mn | Si | Cr | Mo |
|---|---|---|---|---|
| 0.06 | 1.1 | 0.4 | 1.2 | 0.5 |
All weld metal mechanical properties
| Rm (MPa) | Rp0.2 (Mpa) | A5 (%) | KCV | |
|---|---|---|---|---|
| 630 | 530 | 24 | 20°C: 120 J | PWHT 1h/690°C |
Shielding gas
| M21 gas mixtures (Ar + 5 - 25% CO2) according to EN 439 / ISO 14175 | Gas flow rate: 12 - 25 l/min |
|---|
Operating conditions
| Diameter [mm] | Current type | Current I [A] | Voltage [V] | Stick out [mm] |
|---|---|---|---|---|
| 1.2 | DC(+) or pulsed | 100-350 | 15-35 | 12-25 |
| 1.4 | DC(+) or pulsed | 120-400 | 15-35 | 12-25 |
| 1.6 | DC(+) or pulsed | 130-450 | 15-35 | 15-25 |
Welding positions
FCW M CrMo1 is primarily used in the flat and horizontal-vertical positions. However, welds in other positions are also possible using the short-circuiting or pulsed arc modes of transfer.
Packings & Diameters
| Diameters [mm] | 1.2 - 1.4 - 1.6 |
|---|---|
| Packing(s) | Spool BS300 |
| Weight [Kg] | 15 |