Abrafonte
Pure nickel electrode
Descripción y aplicaciones
Electrode with a graphite-basic coating. Weld deposit consists of pure nickel. Recommended for cold welding and repairing of grey cast iron, repairing of cracks. Homogeneous and easy to machine deposit. Good bonding and flow of the weld metal.
Main applications:
Repairing of engine blocks, frames of tool machines, gearboxes, reducing pieces, valve and pump bodies.
Grey cast iron to different steels:
|
NF A 32-101 |
: |
FGL 150, 200, 250, 300, 350, 400 |
|
NF A 32-201 |
: |
FGS 370-17, 400-12, 500-7, 600-3, 700-2 |
|
NF A 32-702 |
: |
MN 350-10, 380-18, 450-6, 350-4, 650-3 |
|
DIN 1691 |
: |
CG-14, 18, 25, 30 |
|
DIN 1693 |
: |
GGG-40, 50, 60, 70 |
|
DIN 1692 |
: |
GTS-35, 45, 55, 65, 70 |
Clasificación
| NF A 81-342 | AWS A 5.15 | DIN 8573 | EN ISO 1071 |
|---|---|---|---|
| E Ni BG 11 | E Ni-CI | E Ni BG 11 | E C Ni-CI 3 |
Análisis químico (%)
| C | Mn | Si | Fe | Ni |
|---|---|---|---|---|
| 1.2 | <1.0 | <2.0 | <2.0 | >95.0 |
Propiedades mecánicas
| Rm (MPa) | Hardness |
|---|---|
| >300 | approx. 180 HB |
Diámetros disponibles
| Diámetro | 2.5x350 - Standard Pack | 2.5x350 - Small Pack | 3.2x350 - Standard Pack | 3.2x350 - Small Pack | 4.0x350 - Standard Pack | 4.0x350 - Small Pack | 5.0x450 - Standard Pack | 5.0x450 - Small Pack |
|---|---|---|---|---|---|---|---|---|
| Piezas / estuche | 251 | 50 | 156 | 31 | 100 | 20 | 66 | 10 |
| Piezas / paquete | 1004 | 1000 | 624 | 620 | 400 | 400 | 264 | 200 |
| Kg 1000 electr. | 19.9 | 19.9 | 32 | 32 | 50 | 50 | 98 | 98 |
| Estuche / paquete | 4 | 20 | 4 | 20 | 4 | 20 | 4 | 20 |
| Kg / estuche | 5 | 1 | 5 | 1 | 5 | 1 | 6.5 | 1 |
| Kg / paquete | 20 | 20 | 20 | 20 | 20 | 20 | 26 | 20 |
Amperaje
| A | 70 | 70 | 100 | 100 | 145 | 145 | 180 | 180 |
|---|
Condiciones de uso
Weld on clean and exempt from grease surfaces (previous grinding of the joint). Apply a heat input as low as possible and keep the temperature low ( < 70°C). Weld with lowest practical current and depose short and narrow beads to reduce the risk of producing cracks in the base metal. To reduce stresses, produced during welding, hammering of the beads is recommended after the deposition of short runs (essential on rigid pieces).
= + -
~ 40V